HD-AW-8880 is double-component rigid PU foam system specially designed for manufacturing imitation wood PU products. B-component is modified polyisocyanate(MDI), while A-component is made up of polyether polyalcohol,blowing agent,catalyst and stabiliser,etc. HD-AW-8880 has two kinds of brands.
* HD-AW-8880H is applied to imitation wood PU products with higher hardness and density, such as furniture-bed frames, chairs and desks, windows and doors, furnitures and construction ornaments.
* HD-AW-8880M is applied to imitation wood PU products with medium hardness and density, such as indoor decorative bars,imitation plate, art relief, artwares and toys.
Physical Properties:
A Component | B Component | ||
Item | Index | Item | Index |
Hydroxy Content (MgKOH/g) | 400±50 | -NCO Content(%) | 30-33 |
Viscosity (25℃)(MPa.s) | 800±100 | Viscosity (25℃)(MPa.s) | 200±40 |
Specific Gravity (25℃)(g/cm3) | 1.18±0.05 | Specific Gravity (25℃)(g/cm3) | 1.235±0.02 |
Reaction Time | HD-AW-8880H | HD-AW-8880M |
CT(sec) | 30-35 | 28-32 |
GT(sec) | 80-105 | 65-72 |
RT(sec) | 100-110 | 95-102 |
DMT(sec) | 480±60 | 300±60 |
Foam Performance:
Item | HD-AW-8880H | HD-AW-8880M | Testing Method |
Moulding Density (kg/m3) | 250-400 | 160-250 | ISO845 |
Freedom Density (kg/m3) | 120-200 | 90-120 | ISO845 |
Product Shrinkage Ratio (%) | 0.4-0.6 | 0.5-0.7 | --- |
Thermal Conductivity (W/m.K) | 0.07-0.08 | 0.06-0.07 | ISO2582 |
Surface Hardness (Shore D) | 35-55 | 25-45 | ASTMD2240-68 |
High-temperature Resistance (℃) | 70-110 | 70-110 | ASTMD648-56 |
Breaking Strength (MPa) | 20-25 | 25-30 | ASTMD790-71 |
Packaging:Galvanized Zinc Metal Barrel Packag A Component:200kg/barrel;B Component:250kg/barrel
Shelf Life:6 Months